PPA
品名
美国苏威
厂家(产地)
FC-1150
牌号
注塑
加工级别
邓女士
主营: 橡胶和塑料制品业
广东省东莞市
Amodel® FC-1150 and FC-1150 L is an FDA compliant, 50% glass fiber reinforced resin designed for high strength and stiffness (and improved demolding properties for the L grades). This combines with its excellent thermal properties, low water absorption and good hydrolytic stability to make it particularly suited for components used in food service and consumer applications such coffee machines and ovens.
- Natural: FC-1150 (L) NT
- Black: FC-1150 (L) BK 946
Key Attributes: Chemical Resistant; Chlorine Resistant; Creep Resistant; Good Dimensional Stability; Good Stiffness; High Stiffness; High Strength; High Temperature Strength; Low Moisture Absorption
Applications: Appliances; Housings; Non-specific Food Applications; Plumbing Parts; Pump Parts
Agency Ratings: EU 10/2011; FDA 21 CFR 176.170(c); NSF STD-51
Injection Notes: Mold Temperature:
- Higher tool temperatures might be required for thin wall sections
Storage:
- Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. Manufacturer recommendeds that Amodel® resins be dried prior to molding.
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.67 g/cc | 0.0603 lb/in3 | Method A; ISO 1183 |
Linear Mold Shrinkage, Flow | 0.0014 - 0.0016 cm/cm @Thickness 1.00 mm | 0.0014 - 0.0016 in/in @Thickness 0.0394 in | ASTM D255 |
0.0015 - 0.0018 cm/cm @Thickness 2.00 mm | 0.0015 - 0.0018 in/in @Thickness 0.0787 in | ASTM D255 | |
Linear Mold Shrinkage, Transverse | 0.0042 - 0.0043 cm/cm @Thickness 2.00 mm | 0.0042 - 0.0043 in/in @Thickness 0.0787 in | ASTM D255 |
0.0042 - 0.0046 cm/cm @Thickness 1.00 mm | 0.0042 - 0.0046 in/in @Thickness 0.0394 in | ASTM D255 | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 270 MPa @Temperature 23.0 °C | 39200 psi @Temperature 73.4 °F | ISO 527-2 |
Elongation at Break | 2.0 % @Temperature 23.0 °C | 2.0 % @Temperature 73.4 °F | ISO 527-2 |
Tensile Modulus | 19.1 GPa | 2770 ksi | ISO 527-2 |
Flexural Strength | 400 MPa | 58000 psi | ISO 178 |
Flexural Modulus | 18.4 GPa @Temperature 23.0 °C | 2670 ksi @Temperature 73.4 °F | ISO 178 |
Flexural Strain at Break | 2.4 % | 2.4 % | ISO 178 |
Charpy Impact Unnotched | 8.80 J/cm2 | 41.9 ft-lb/in2 | ISO 179 |
特性
PPA强度、韧度和硬度优越性能,以及其良好的耐热件,耐化学性及抗开裂能力
PPA由于高温和高湿环境下仍能保持强度和硬度,可在传统的尼龙和聚酯所无法随的就用中替换金属
PPA塑料还具有优越的表面光泽性。可以对其进行着色而避免了表面喷涂,从而有助于降低表面划痕和刮痕的明显程度。
PPA塑料还具有良好的可加工性,并允许短的注塑循环时间
与PA46相比:
PPA具有比PA46更高的热稳定性;
PPA具有比PA46更好的CTI/耐电弧能和红外同流能力;
PPA具有比PA46更好的耐化学性;
应用
汽车部件,包括燃油、传动及发动机系统,可减轻重量、降低成本并提供长时间的使用寿命;
芯片组和插座、杯体焊接支座;
片状电容器、开关及微型喇叭、制作高密度的印刷电路板连接器;
用于耐磨要求极高的场合,例如无润滑轴承、密封、轴承隔离环和往复开压缩机零件;
连接器、控制器、传感器、马达及其它关键电子部件
阻燃PPSU RADEL R-5600
COC TOPAS 6013S-04 耐化学性
高耐热性COC 德国TOPAS 6013M-07
PA46 STANYL TW300 荷兰DSM
热稳定PA46 STANYL 46SF5030
荷兰DSM PA46 STANYL 46HF5050
热稳定PA46 STANYL 46SF5030
荷兰DSM PA46 STANYL 46HF5050
30%玻璃纤PA46 STANYL 46HF4130
抗冲击性ABS POLIMAXX MH-1
泰国普力迈ABS POLIMAXX KU650
高抗冲击性ABS POLIMAXX GA850
*采购数量: 公斤
采购数量不能为空
*联系信息:
联系信息不能为空
公司名称:
采购说明:
验证码不正确