Product Description
TOPAS 8007F-04 is a general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer cast applications, and in coextrusions in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as blister, twist, barrier, shrink and easy tear packaging. Industrial uses include formed decorative sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended.

Selected Applications

• Pharmaceutical blisters

• Deep draw barrier trays

• Shrink films and labels

• Twist films

• Decorative sheet

• Food packaging

• Healthcare and food contact

Leading Attributes

• Clarity, forming, barrier, purity, halogen-free

• Excellent deep forming, unlike other barriers

• High shrink, low stress, gloss, clarity, toughness

• High gloss, outstanding deadfold, clean cutting

• Gloss, hardness, chemical resistance, forming

• Not manufactured with BPA, phthalates, or halogens

• Broad regulatory compliance

Related Grades for Packaging and Film Extrusion

• TOPAS 8007F-400 - robust extrusion grade especially for PE blends

• TOPAS 8007F-600 - robust clarity extrusion grade especially for PE blends

TOPAS? 8007F-04 物性表

基本信息
特性	纯度高 防潮 刚性，高 高光 共聚物 耐化学性良好 清晰度，高 韧性良好 食品接触的合规性 通用 无 BPA 无定形的 无卤
用途	包装 薄膜 标签 流延薄膜 片材 食品包装 通用 药品包装 医疗/护理用品
机构评级	DMF 12132 FDA FCN 405 欧洲 10/1/2011 12:00:00 AM
形式	粒子
加工方法	薄膜挤出 吹塑薄膜 共挤薄膜 流延薄膜 热成型

物理性能	额定值	单位制	测试方法
密度	1.02	g/cm3	ISO 1183
熔流率（熔体流动速率）			ISO 1133
190°C/2.16 kg	1.8	g/10 min	ISO 1133
230°C/2.16 kg	11	g/10 min	ISO 1133
溶化体积流率（MVR）			ISO 1133
190°C/2.16 kg	2.00	cm3/10min	ISO 1133
230°C/2.16 kg	12.0	cm3/10min	ISO 1133
吸水率(饱和, 23°C)	0.010	%	ISO 62

薄膜	额定值	单位制	测试方法
薄膜厚度 - 经测试	70	μm
拉伸模量			ISO 527-3/1
MD : 70 μm, 铸造薄膜	2200	MPa	ISO 527-3/1
TD : 70 μm, 铸造薄膜	1800	MPa	ISO 527-3/1
拉伸应力			ISO 527-3/50
MD : 断裂, 70 μm, 铸造薄膜	57.0	MPa	ISO 527-3/50
TD : 断裂, 70 μm, 铸造薄膜	50.0	MPa	ISO 527-3/50
伸长率			ISO 527-3/50
MD : 断裂, 70 μm, 铸造薄膜	2.9	%	ISO 527-3/50
TD : 断裂, 70 μm, 铸造薄膜	3.0	%	ISO 527-3/50
落锤冲击(70 μm, 铸造薄膜)	36	g	ISO 7765-1
埃尔曼多夫抗撕强度			ISO 6383-2
MD : 70 μm, 铸造薄膜	2.2	N	ISO 6383-2
TD : 70 μm, 铸造薄膜	2.3	N	ISO 6383-2
透氧率(23°C, 70 μm, 挤塑薄膜, 50% RH)	25	cm3·mm/m2/atm/24 hr	ASTM D3985
水气透过率(70 μm, 23°C, Cast Film, 85% RH)	0.094	g·mm/m2/atm/24 hr	ASTM F1249

热性能	额定值	单位制	测试方法
玻璃转化温度	78.0	°C	ISO 11357-2

光学性能	额定值	单位制	测试方法
光泽度(60°, 70.0 μm, 铸造薄膜)	100		ISO 2813
雾度(70.0 μm, 铸造薄膜)	1.0	%	ISO 14782

挤出	额定值	单位制
挤塑机进料部分	20 到 60	°C
挤出机螺杆长径比L / D	28:1
料筒1区温度	210 到 220	°C
料筒2区温度	230 到 240	°C
料筒3区温度	230 到 240	°C
料筒4区温度	230 到 240	°C
口模温度	230 到 240	°C