Product Description: HTA 001HD is a high weight HDPE film grade. Films made from HTA 001HD exhibit excellent impact and toughness properties as well as high stiffness.
Availability: Africa & Middle East and Asia Pacific
Additive:
Applications:
Information provided by ExxonMobil
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D4883 |
Melt Flow | 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 9.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
Mechanical Properties | Metric | English | Comments |
Film Tensile Strength at Yield, MD | 40.7 MPa | 5900 psi | ASTM D882 |
Film Tensile Strength at Yield, TD | 30.3 MPa | 4400 psi | ASTM D882 |
Film Elongation at Break, MD | 220 % | 220 % | ASTM D882 |
Film Elongation at Break, TD | 430 % | 430 % | ASTM D882 |
Elmendorf Tear Strength MD | 8.0 g | 8.0 g | ASTM D1922 |
Elmendorf Tear Strength TD | 30 g | 30 g | ASTM D1922 |
Dart Drop Test | 190 g | 0.419 lb | ASTM D1709A |
Film Tensile Strength at Break, MD | 59.3 MPa | 8600 psi | ASTM D882 |
Film Tensile Strength at Break, TD | 55.8 MPa | 8100 psi | ASTM D882 |
1% Secant Modulus, MD | 1170 MPa | 170000 psi | ASTM D882 |
1% Secant Modulus, TD | 1170 MPa | 170000 psi | ASTM D882 |
阻燃PPSU RADEL R-5600
COC TOPAS 6013S-04 耐化学性
高耐热性COC 德国TOPAS 6013M-07
PA46 STANYL TW300 荷兰DSM
热稳定PA46 STANYL 46SF5030
荷兰DSM PA46 STANYL 46HF5050
热稳定PA46 STANYL 46SF5030
荷兰DSM PA46 STANYL 46HF5050
30%玻璃纤PA46 STANYL 46HF4130
抗冲击性ABS POLIMAXX MH-1
泰国普力迈ABS POLIMAXX KU650
高抗冲击性ABS POLIMAXX GA850
*采购数量: 公斤
采购数量不能为空
*联系信息:
联系信息不能为空
公司名称:
采购说明:
验证码不正确