电极红铜分类

紫铜类（纯铜）：T2.C1100.C11000.无氧铜TU1.C1020.C10200加磷脱氧铜TP2.C1220.C12200.

黄铜类，铜合金

H96.C2100.C21000.H90.C2200.C22000.H85.C2300.C23000.H80.C2400.C24000.H68A.C2680.  C26200.H65.C2700.C26800.H62.C2720.C27400.

铅黄铜    HPb59-1.C3710.C37800.HPb59-2.C3771.C35300.  HPb60-2.C3604.C36000.HPb63-3.C3560.C34500.HPb63-0.1.C34900.

铝黄铜HAi77-2.C6870.C68700.  HAi60-1-1.C6782.C67000.HAi59-3-2.C67800.HAi66-6-3-2.C6872.

锡黄铜HSn62-1.HSn70-1AB.锰黄铜HMn58-2.C67400.HMn57-3-1.铁黄铜HFe59-1-1.C6782.C67820.硅黄铜HSi80-3.C69400.

青铜类：

锡青铜QSn4-3,QSn6.5-0.1.QSn7-0.2.C5212.C52100.QSn6.5-0.4.

铝青铜QAi9-2.C61000.QAi9-4.QAi10-3-1.5.  C6161.C61900.QAi10--4-4.C6301.C63000.C63200.

硅青铜QSi3-1.C65500.C65800.QSi1-3.C64700.QSi1.8.  锰青铜QMn5.锆青铜QZr0.2-0.4.铬青铜QCr0.5.C18100.C18200.C18400.QCr1-2.

铬锆铜QCr1-0.15.C18150.  镉青铜QCd1.0.铍青铜QBe1.8.QBe2.0.白铜类：B19.B25.铁白铜BFe10-1--1.B111.C70600.BFe30--1-1.B111.  C71500.

锌白铜BZn15-20.等。

电极红铜

铜+银 CuAg：≥99.90

锡 Sn ：≤0.002 　　

纯铜C1100

锌 Zn：≤0.005 　　

铍 Sb ：≤0.002 　　

镍 Ni：≤0.005 　　

铅 Pb：≤0.005 　　

性能特点与使用说明：有良好的导电，导热，耐蚀和加工性能,常用作导电，导热，耐蚀器材，

C1100纯铜热处理规范：热加工温度900～1050℃;退火温度500～700℃;冷作硬化铜的再结晶开始温度200～300℃。

氧 O：≤0.06 　　

铁 Fe：≤0.005 　　

垫，钉，油管及其他管道。

40Cr——使用最广泛的钢种之一，属合金结构钢

主要特征: 经调质处理后，具有良好的综合力学性能、低温冲击韧度及低的缺口敏感性，淬透性良好，油冷时可得到较高的疲劳强度，水冷时复杂形状的零件易产生裂纹，冷弯 塑性中等，回火或调质后切削加工性好，但焊接性不好，易产生裂纹，焊前应预热到100～150℃，一般在调质状态下使用，还可以进行碳氮共渗和高频表面淬 火处理。

应用举例：调质处理后用于制造中 速、中载的零件，如机床齿轮、轴、蜗杆、花键轴、顶针套等，调质并高频表面淬火后用于制造表面高硬度、耐磨的零件，如齿轮、轴、主轴、曲轴、心轴、套筒、 销子、连杆、螺钉螺母、进气阀等，经淬火及中温回火后用于制造重载、中速冲击的零件，如油泵转子、滑块、齿轮、主轴、套环等，经淬火及低温回火后用于制造 重载、低冲击、耐磨的零件，如蜗杆、主轴、轴、套环等，碳氮共渗处即后制造尺寸较大、低温冲击韧度较高的传动零件，如轴、齿轮等。