Product Description
TOPAS 6013F-04 is a high temperature, general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer and blended cast applications, and in coextrusions and blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS.
Selected Applications
Pharmaceutical blisters
Decorative film and sheet
General packaging
Food packaging
Healthcare and food contact
Leading Attributes
Clarity, forming, barrier, heat resistance, halogen-free
Gloss, hardness, chemical resistance, forming
Easy or linear tear, heat resistance, hot fill
Not manufactured with BPA, phthalates, or halogens
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 1.02 | g/cm3 | ISO 1183 |
熔流率(熔体流动速率) (230°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
溶化体积流率(MVR) (230°C/2.16 kg) | 1.00 | cm3/10min | ISO 1133 |
吸水率 (饱和, 23°C) | 0.010 | % | ISO 62 |
薄膜 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
薄膜厚度 - 经测试 | 70 | μm | |
拉伸模量 | ISO 527-3/1 | ||
MD : 70 μm, 铸造薄膜 | 2400 | MPa | ISO 527-3/1 |
TD : 70 μm, 铸造薄膜 | 2250 | MPa | ISO 527-3/1 |
拉伸应力 | ISO 527-3/50 | ||
MD : 断裂, 70 μm, 铸造薄膜 | 55.0 | MPa | ISO 527-3/50 |
TD : 断裂, 70 μm, 铸造薄膜 | 45.0 | MPa | ISO 527-3/50 |
伸长率 | ISO 527-3/50 | ||
MD : 断裂, 70 μm, 铸造薄膜 | 2.4 | % | ISO 527-3/50 |
TD : 断裂, 70 μm, 铸造薄膜 | 2.2 | % | ISO 527-3/50 |
落锤冲击 (70 μm, 铸造薄膜) | < 36 | g | ISO 7765-1 |
埃尔曼多夫抗撕强度 | ISO 6383-2 | ||
MD : 70 μm, 铸造薄膜 | 0.088 | N | ISO 6383-2 |
TD : 70 μm, 铸造薄膜 | 0.088 | N | ISO 6383-2 |
透氧率 (23°C, 70 μm, 挤塑薄膜, 50% RH) | 28 | cm3·mm/m2/atm/24 hr | ASTM D3985 |
水气透过率 (70 μm, 38°C, Cast Film, 90% RH) | 0.16 | g·mm/m2/atm/24 hr | ASTM F1249 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
玻璃转化温度 | 138 | °C | ISO 11357-2 |
光学性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
光泽度 (60°, 70.0 μm, 铸造薄膜) | > 100 | ISO 2813 | |
雾度 (70.0 μm, 铸造薄膜) | < 1.0 | % | ISO 14782 |
阻燃PPSU RADEL R-5600
COC TOPAS 6013S-04 耐化学性
高耐热性COC 德国TOPAS 6013M-07
PA46 STANYL TW300 荷兰DSM
热稳定PA46 STANYL 46SF5030
荷兰DSM PA46 STANYL 46HF5050
热稳定PA46 STANYL 46SF5030
荷兰DSM PA46 STANYL 46HF5050
30%玻璃纤PA46 STANYL 46HF4130
抗冲击性ABS POLIMAXX MH-1
泰国普力迈ABS POLIMAXX KU650
高抗冲击性ABS POLIMAXX GA850
*采购数量: 公斤
采购数量不能为空
*联系信息:
联系信息不能为空
公司名称:
采购说明:
验证码不正确