Amodel® DW-1140 is a 40% glass-fiber-reinforced resin designed for high strength and stiffness and improved hydrolytic stability. This material has low moisture absorption and a low coefficient of thermal expansion, which means excellent dimensional stability. Creep resistance is also exceptional.
This grade has been approved for use with potable water in the United States, France, Germany, and the United Kingdom.
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 1.55 | g/cm3 | ISO 1183/A |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | 14000 | MPa | ISO 527-2 |
拉伸应力 (断裂, 23°C) | 230 | MPa | ISO 527-2 |
拉伸应变 (断裂, 23°C) | 2.0 | % | ISO 527-2 |
弯曲模量 (23°C) | 14000 | MPa | ISO 178 |
弯曲强度 (断裂, 23°C) | 330 | MPa | ISO 178 |
断裂弯曲应变 (23°C) | 2.5 | % | ISO 178 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
简支梁缺口冲击强度 | 9.3 | kJ/m2 | ISO 179 |
简支梁无缺口冲击强度 | 63 | kJ/m2 | ISO 179 |
悬壁梁缺口冲击强度 | 9.0 | kJ/m2 | ISO 180 |
PPA (Polyphthalamide ) 聚邻苯二甲酰胺,在高温高湿状态下,PPA的抗拉强度比尼龙6高20%,比尼龙66更高;PPA材料的弯曲模量比尼龙高20%,硬度更大,能抗长时间的拉伸蠕变;且PPA的耐汽油、耐油脂和冷却剂的能力也比PA强;一种耐高温尼龙,这种材料可以耐200℃的持续高温,并且还能保持良好的尺寸稳定性 [1] 。
聚邻苯二甲酰胺(简称PPA)树脂是以对苯二甲酸或间苯二甲酸为原料的半芳香族聚酰胺。既有半结晶态的,也有非结晶态的,其玻璃化温度在255°F左右。非结晶态的PPA主要用于要求阻隔性能的场合;半结晶态的PPA树脂主要用于注塑加工,也用于其它熔融加工工艺。下文主要介绍后者——半结晶态PPA树脂,特别注明的除外。半结晶态PPAS的熔点约为590°F,以不透明矩形切片的形式供应。
聚邻苯二酰胺(简称PPA)树脂是以对苯二甲酸或邻苯二甲酸为原料的半芳香族聚酰胺。既有半结晶态的,也有非结晶态的,其玻璃化温度在255°F左右。非结晶态的PPA主要用于要求阻隔性能的场合;半结晶态的PPA树脂主要用于注塑加工,也用于其它熔融加工工艺下文主要介绍后者——半结晶态PPA树脂,特别注明的除外。半结晶态PPAS的熔点约590°F,以不透明矩形切片的形式供应。
阻燃PPSU RADEL R-5600
COC TOPAS 6013S-04 耐化学性
高耐热性COC 德国TOPAS 6013M-07
PA46 STANYL TW300 荷兰DSM
热稳定PA46 STANYL 46SF5030
荷兰DSM PA46 STANYL 46HF5050
热稳定PA46 STANYL 46SF5030
荷兰DSM PA46 STANYL 46HF5050
30%玻璃纤PA46 STANYL 46HF4130
抗冲击性ABS POLIMAXX MH-1
泰国普力迈ABS POLIMAXX KU650
高抗冲击性ABS POLIMAXX GA850
*采购数量: 公斤
采购数量不能为空
*联系信息:
联系信息不能为空
公司名称:
采购说明:
验证码不正确